Comparative Evaluation of Bond Strength of Self-Etching and Total Etch Dental Adhesive Systems to Dentin of Deciduous and Permanent Teeth / Evaluación Comparativa de la Fuerza de Unión de los Sistemas de Adhesivo Dental Autograbado y Grabado Total para la Dentina de Dientes Deciduos y Permanentes

ABSTRACT: The aim of this study was to analyze the bond strength of total-etch and self-etch adhesive systems to dentin of primary and permanent teeth. Methods: Thirty sound naturally exfoliated primary molars deciduous teeth (DT) and thirty sound permanent bicuspids permanent teeth (PT) were randomly divided into six groups (n=10 per group) according to two commercial adhesive systems: Adper Single Bond 2; 3M ESPE (Total-etch) and Adper Easy Bond; 3M ESPE (selfetch and total-etch). Specimens submitted to cyclic loading in a universal Instron testing machine. Bond strength values (MPa) were analyzed by ANOVA test and Duncan post hoc test (a=0.05). Results: Mean values were higher in PT compared to DT. In deciduous teeth, no significantly differences observed. Total etch AdperTM Single Bond 2 showed significantly higher bond strength than self-etch AdperTM with additional acid etching in PT (p=0.031). Conclusion: Our findings suggest that the highest bond strength was found in dentin tissue of PT with total etch AdperTM employing the adhesive the Single Bond 2 of one step self-etch.

RESUMEN: El objetivo de este estudio fue analizar la fuerza de unión de los sistemas adhesivos de grabado total y autograbado a la dentina de los dientes primarios y permanentes. Métodos: treinta sonidos exfoliaron naturalmente los molares primarios dientes caducifolios (DT) y treinta sonidos. Los dientes permanentes de los premolares permanentes (PT) se dividieron aleatoriamente en seis grupos (n = 10 por grupo) de acuerdo con dos sistemas adhesivos comerciales: Adper Single Bond 2; 3M ESPE (Grabado total) y Adper Easy Bond; 3M ESPE (autograbado y grabado total). Muestras sometidas a carga cíclica en una máquina universal de pruebas Instron. Los valores de resistencia de la unión (MPa) se analizaron mediante la prueba ANOVA y la prueba post hoc de Duncan (a = 0.05). Resultados: Los valores medios fueron mayores en PT en comparación con DT. En dientes deciduos, no se observaron diferencias significativas. Total etch AdperTM Single Bond 2 mostró una fuerza de unión significativamente mayor que la autograbado AdperTM con grabado ácido adicional en PT (p = 0.031). Conclusión: Nuestros hallazgos sugieren que la mayor fuerza de unión se encontró en el tejido de dentina de PT con grabado total AdperTM empleando el adhesivo Single Bond 2 de autograbado de un solo paso.

Non-thermal plasma increase bond strength of zirconia to a resin cement / Plasma não-térmico aumenta a resistência de união da zircônia a um cimento resinoso

Objective: This study investigated the influence of different surface treatments on zirconia surface energy, roughness and microshear bond strength. Material and Methods: Forty eight slices of Yttriastabilized tetragonal zirconia polycrystal (Y-TZPVITA In-Ceram® YZ for inLab®) (6.4 x 3.2 x 1.6 mm) were divided into 3 groups according to the surface treatment (n = 16): YTZP_control -untreated; YTZP_plasma -surface treatment with non-thermal oxygen plasma; YTZP_primer - coating with ceramic primer. Surface energy (n = 6) was measured with a goniometer; and surface roughness (n = 10) was analyzed with a 3D profilometer were performed over zirconia surface. On the same specimens of surface roughness, on the treated zirconia's surface, resin cement (PANAVIA V5 - Kuraray Noritake Dental) was built up by inserting the resin cement into Tygon tubes (1 mm of internal diameter X 1 mm length). After 24h storage, microshear test was assessed. Data were analyzed by one-way ANOVA and Tukey posthoc test (p < 0.05). Results: Nonthermal oxygen plasma treated specimens exhibited higher statistically significant surface energy (p = 0.00) and bond strength (p = 0.00) when compared to control and primer groups. Roughness test (p = 0.897) could not detect statistical difference among the tested groups. Conclusion: Non-thermal oxygen plasma should be a suitable alternative for zirconia surface treatment prior to luting hence it improved microshear bond strength and provided higher surface energy without affecting surface roughness. (AU)

Objetivo: Este estudo investigou a influência de diferentes tratamentos de superfície na energia de superfície, rugosidade e resistência de união da zircônia. Material e Métodos: Quarenta e oito fatias de zircônia tetragonal policristalina estabilizada por ítria (Y-TZP - VITA InCeram® YZ for inLab®) (6,4 x 3,2 x 1,6 mm) foram divididas em 3 grupos de acordo com o tratamento de superfície (n = 16): YTZP_controle sem tratamento; YTZP_plasma - tratamento de superfície com plasma de oxigênio não térmico; YTZP_primer - aplicação de um primer cerâmico. A energia da superfície (n = 6) foi medida com o auxilio de um goniômetro; e a rugosidade superficial (n = 10) foi analisada com um perfilômetro 3D. Nos mesmos espécimes da rugosidade, prolongamentos de cimento resinoso (PANAVIA V5 - Kuraray Noritake Dental) foram construídos inserindo o cimento em micro túbulos de silicone (1mm de diâmetro interno de X 1 mm de comprimento). O teste de microcisalhamento foi realizado após 24h. Os dados foram analisados estatisticamente ANOVA um fator e teste auxiliar de Tukey (p < 0,05). Resultados: Os espécimes tratados com plasma de oxigênio apresentaram maiores valores de energia de superficie (p = 0,00) e resistência de união estatisticamente significante (p = 0,00) quando comparados aos grupos controle e do primer. A análise de rugosidade (p = 0,897) não detectou diferença estatística entre os grupos testados. Conclusão: O plasma não térmico pode ser uma alternativa para o tratamento de superfície de zircônia antes da cimentação, pois aumentou a resistência de união ao microcilsalhamento e proporcionou maior energia superficial sem afetar a rugosidade da superfície. (AU)

Estudo in vitro do nível de escoamento de cinco cimentos endodônticos: Endofill, AH Plus, MTA Fillapex, Sealer 26 e Pulp Canal Sealer EWT / In vitro study of the flow rate of five root canal sealers: Endofill, AH Plus, MTA Fillapex, Sealer 26 and Pulp Canal Sealer EWT

Objetivo: o objetivo desse trabalho foi estudar, in vitro, o nível de escoamento dos cimentos Endofill, AH Plus, MTA Fillapex, Sealer 26 e Pulp Canal Sealer EWT. Métodos: os cimentos foram manipulados de acordo com as recomendações dos fabricantes. A determinação do escoamento foi conseguida em conformidade com a especificação #57 da ADA (American Dental Association). Na comparação entre os grupos, foi realizada a ANOVA (análise de variância) e posterior teste de Tukey, com nível de confiança de 95%. Resultados: os resultados mostraram que o cimento MTA Fillapex apresentou o maior escoamento entre os cimentos estudados e o cimento AH Plus foi o único que apresentou escoamento estatisticamente significativo após 24 e 48 horas. Conclusão: concluiu-se que todos os cimentos avaliados estão em conformidade com a especificação #57 da ADA. No entanto, o cimento MTA Fillapex foi superior aos outros cimentos analisados, no que se refere ao poder de escoamento. O desempenho clínico do cimento obturador está diretamente relacionado à sua capacidade de penetrar nos túbulos dentinários e canais laterais; daí a importância do estudo do escoamento dos cimentos endodônticos.

Sistemas adesivos - classificação / Adhesives systems - classification

Os adesivos dentários são combinações de monômeros resinosos hidrofílicos e hidrofó- bicos, de diferentes pesos moleculares e solventes, que estabelecem ligação entre o material restaurador e a estrutura dentária após polimerização. Sistemas adesivos atuais são indicados para diversas aplicações odontológicas e classificados como condicionamento total (etch-and- -rinse) ou autocondicionamento (self-etching) e sua intenção de uso difere no número de etapas de aplicação e como eles interagem com as estruturas dentais naturais.

Dentin adhesives are combinations of hydrophilic and hydrophobic monomers, with different molecular weights and solvents that connect the restorative material to the tooth structure after polymerization. Current adhesive systems are suitable for various dental applications and classified as etch-and-rinse or self-etching. The purpose of their use differs according to the number of application steps and how they interact with the natural dental structures.

Effect of cement type and water storage time on the push-out bond strength of a glass fiber post

This study investigated the effects of the cement type and the water storage time on the push-out bond strength of a glass fiber post. Glass fiber posts (Fibrekor, Jeneric Pentron) were luted to post spaces using a self-cured resin cement (C&B Cement [CB]), a glass ionomer cement (Ketac Cem [KC]) or a resin-modified glass ionomer cement (GC FujiCEM [FC]) according to the manufacturers’ instructions. For each luting agent, the specimens were exposed to one of the following water storage times (n=5): 1 day (T1), 7 days (T7), 90 days (T90) and 180 days (T180). Push-out tests were performed after the storage times. Control specimens were not exposed to water storage, but subjected to the push-out test 10 min after post cementation. Data (in MPa) were analyzed by Kruskal-Wallis and Dunn`s test (α=0.05). Cement type and water storage time had a significant effect (p<0.05) on the push-out bond strength. CB showed significantly higher values of retention (p<0.05) than KC and FC, irrespective of the water storage time. Water storage increased significantly the push-out bond strength in T7 and T90, regardless of the cement type (p<0.05). The results showed that fiber posts luted to post spaces with the self-cured resin cement exhibited the best bonding performance throughout the 180-day water storage period. All cements exhibited a tendency to increase the bond strength after 7 and 90 days of water storage, decreasing thereafter.

Este estudo investigou os efeitos do tipo de cimento e do tempo de armazenamento em água na resistência adesiva ao cisalhamento de pinos de fibra. Pinos de fibra de vidro (Fibrekor, JenericPentron) foram cimentados aos condutos radiculares usando o cimento resinoso autopolimerizável (C&B Cement [CB]), o cimento de ionômero de vidro (Ketac Cem [KC]) ou o cimento de ionômero de vidro modificado por resina (GC FujiCEM [FC]) de acordo com as instruções dos fabricantes. Para cada cimento, os espécimes foram expostos a um dos seguintes tempos de armazenamento em água (n=5): 1 dia (T1), 7 dias (T7), 90 dias (T90) e 180 dias (T180). Os testes de resistência adesiva ao cisalhamento foram realizados após os períodos de armazenamento. Os espécimes controles não foram expostos ao armazenamento em água, mas submetidos ao teste de resistência adesiva ao cisalhamento 10 min após a cimentação do pino. Os dados (MPa) foram analisados usando Kruskal-Wallis e teste de Dunn (α=0,05). O tipo de cimento e o tempo de armazenamento em água afetaram significantemente a resistência adesiva ao cisalhamento (p<0,05). CB apresentou valores de retenção significantemente superiores a KC e FC, independentemente do tempo de armazenamento em água. Esse, por sua vez, aumentou significantemente a resistência adesiva ao cisalhamento em T7 e T90, independentemente do tipo de cimento (p<0,05). Os resultados indicaram que os pinos de fibra cimentados aos condutos radiculares com o cimento resinoso autopolimerizável apresentou a melhor performance adesiva durante todo o período de armazenamento em água de 180 dias. Todos os cimentos apresentaram uma tendência a aumentar a resistência adesiva ao cisalhamento após 7 e 90 dias de armazenamento em água, diminuindo posteriormente.

Materiales restauradores con desprendimiento de fluoruro y la reincidencia de caries: parte I: antecedentes / Fluoride releasing restorative materials and caries re-incidence: part I: background

El desarrollo de los materiales dentales restauradores con desprendimiento de fluoruro y la prevención de la reincidencia de caries, depende de muchos factores y no necesariamente sólo del efecto terapéutico del fluoruro sobre la estructura del diente. La relación de estos materiales con la presencia de caries secundaria es revisada en este artículo, así como también la evolución de la incorporación de fluoruro a distintos materiales dentales restauradores.

[Shear bond strength of ideal maccoo and brilliant light cure composites in orthodontic bracket bonding to enamel]

Due to the disadvantages of self cure composites, application of light cure composites is suggested in orthodontics but light transmission through metal brackets is in doubt. The aim of this study was to compare shear bond strength [SBS] of Ideal Maccoo and Brilliant composites in bonding steel and ceramic brackets. Eight intact first upper premolars were collected for this experimental invitro study and randomly divided into 4 equal groups. The buccal surfaces were etched and cured by visible light after applying margin bond resin. In the first group Ideal Maccoo composite was applied on the steel bracket base [SI group], bracket positioning in the correct location was done and then curing was performed by visible light for 40 seconds [20 seconds from occlusal and 20 seconds from gingival]. In the second group fascination ceramic brackets with Ideal Maccoo composite [CI group], in the third group ceramic brackets with Brilliant composite [CB group] and in the fourth group steel brackets with Bralliant composite [SB group] were bonded to teeth with the same method. SBS was measured by Zwick testing Machine. To compare the groups, Kolomgrov-Smironov, two way analysis of variance, one way analysis of variance and Tukey tests were used. Mean SBS was 9.71 +/- 3.37, 7.36 +/- 4.40, 5.58 +/- 2.21 and 12.36 +/- 5.77 in SI, CI, CB and SB groups respectively. Tukey test showed significant difference between SB and CB groups [P<0.001], no significant differences was detected between CI and SI, SI and SB and between CI and CB. Ideal Maccoo and Brilliant light cure composites had good capabilities in steel bracket bonding whereas ceramic brackets had lower shear bond strength. In bonding ceramic brackets only Ideal Maccoo composite showed acceptable results

Pit and fissure sealants: an update

Fissure sealants are well-established components in preventive dental care, both for individual patients and in public health programs. Resin pit-and-fissure sealants are considered an important adjunct to oral health care strategies and fluoride therapy in preventing occlusal carious lesions, Occlusal caries accounts for 56% to 70% of the lesions in children aged 5 to 17 years. Fissure sealing is an established and effective approach for caries management on occlusal surfaces. The effectiveness of sealants hinges on their ability to isolate pits and fissures from a combination of bacteria, their nutrients, and acidic metabolic products Consequently, poor sealing ability may cause secondary caries and interfere in long term success of this technique

Fijación de estructuras rígidas en odontología restauradora: una revisión general / Fixation of rigid structures in restorative dentistry: a general review

Las restauraciones rígidas pueden fijarse a través de procedimientos convencionales no adhesivos, semiadhesivos o adhesivos de acuerdo al tipo de restauración, así como a otras variables. Las fijaciones adhesivas exigen el empleo de medios cementantes resinosos y preparaciones superficiales específicas de las superficies a unir. Otorgan algunas ventajas pero convierten el proceso en más complejo, extenso y costoso. Las fijaciones semiadhesivas son alternativas válidas en muchos casos, simplificando el proceso. Es fundamental reconocer las características y necesidades de cada situación clínica para indicar una u otra técnica de fijación.

Microscopic analysis of dog dental pulp after pulpotomy and pulp protection with mineral trioxide aggregate and white Portland cement

Considerando estudos anteriores sobre a similaridade entre a composição química do agregado de trióxido mineral e o cimento Portland, o objetivo deste estudo foi investigar a resposta pulpar de dentes de cães após pulpotomia e proteção pulpar direta com MTA Angelus e cimento Portland branco. Trinta e oito remanescentes pulpares foram recobertos com esses materiais. Cento e vinte dias após o tratamento, os animais foram sacrificados e os espécimes removidos e preparados para análise histológica. Ambos os materiais demonstraram os mesmos resultados quando utilizados como materiais de capeamento pulpar, induzindo a formação de ponte de tecido mineralizado e mantendo a vitalidade pulpar em todos os espécimes. Ambos matérias se mostraram efetivos como protetores pulpares após pulpotomia em dentes de cães.

Efeito do tratamento de superfície de uma cerâmica aluminizada infiltrada de vidro sobre a resistência à microtração / Effect of surface treatment of a glass-infiltrated alumina ceramic on the microtensile bond strength

Este estudo avaliou a resistência à microtração entre um cimento resinoso e uma cerâmica submetida a três tratamentos de superfície. Foram confeccionados 12 blocos da cerâmica In-Ceram Alumina (VITA) e 12 blocos de resina composta (Clearfil APX, Kuraray) com dimensões de 6mm x 6mm x 5mm. A superfície da cerâmica foi polida com lixas d'água nº 600, 800 e 1200 sob refrigeração, e os blocos foram divididos em três grupos conforme o tratamento superficial: Grupo 1 - Jateamento com óxido de alumínio 110µm; Grupo 2 - Sistema Rocatec (3M/ESPE): jateamento com óxido de alumínio 110µm (Rocatec-pre powder) e com sílica (Rocatec-plus powder) + silano (Rocatec-Sil); Grupo 3 - Sistema CoJet (3M/ESPE): jateamento com partículas de sílica 30µm + ESPE-Sil. Os blocos cerâmicos foram cimentados aos de resina composta com o cimento resinoso Panavia F (Kuraray Co) conforme as instruções do fabricante, sob carga de 750g por 10min. As amostras foram armazenadas (água destilada/37ºC/7 dias) e seccionadas em dois eixos, x e y, com disco diamantado sob refrigeração em uma máquina de corte a fim de obter corpos-de-prova (CP) com 0,6±0,1mm² de área adesiva (n=36). Os CP foram fixados em dispositivo adaptado para o teste de microtração e tracionados (velocidade: 0,5 mm.min-1) na máquina de ensaio universal EMIC. Os resultados (MPa) foram submetidos à análise de variância e ao Teste de Tukey (p<0,05) [grupo 1 - 15,36; grupo 2 - 30,98 e grupo 3 - 31,25]. Os grupos 2 (Rocatec) e 3 (CoJet) apresentaram maior resistência adesiva que o grupo 1. Não houve diferença estatística significativa entre os grupos 2 e 3.

Grau de infiltraçäo marginal de duas técnicas restauradoras com cimento de ionômero de vidro em molares decíduos: estudo comparativo in vitro / Microleakage between two filling restorative techniques using glass ionomer cement in primary molars: comparative in vitro study

A técnica do condicionamento ácido e o desenvolvimento e aprimoramento de novos materiais restauradores com características adesivas têm levado a mudanças importantes nas concepçöes e nos princípios da dentística operatória e restauradora. O objetivo deste estudo foi avaliar a microinfiltraçäo marginal em cavidades proximais de molares decíduos restaurados com cimento de ionômero de vidro modificado por resina (Vitremer, 3M) comparando duas diferentes técnicas: a técnica convencional (conforme recomendaçöes do fabricante) e a técnica de hibridizaçäo (ácido fosfórico - 37 por cento e sistema adesivo Scotchbond Multi-Uso, 3M ). Foram utilizados 20 molares decíduos hígidos, onde foram preparadas cavidades proximais. A amostra foi dividida aleatoriamente em 2 grupos. No grupo 1 foi utilizado a técnica convencional e no grupo 2 a técnica com condicionamento ácido e aplicaçäo de sistema adesivo. Os dentes foram submetidos ao processo de ciclagem térmica, impermeabilizados, mantendo uma área de 2mm² na margem cervical da restauraçäo e imersos em soluçäo de azul de metileno a 0,5 por cento, por 72 horas. A seguir, foram seccionados e avaliados por um único examinador, que estabeleceu o grau de microinfiltraçäo. Os dados obtidos revelaram que as duas técnicas utilizadas apresentaram microinfiltraçäo marginal em diferentes graus, e que näo houve diferença estatisticamente significante entre elas

Efeito da ciclagem térmica sobre a resistência de uniäo entre uma cerâmica infiltrada com vidro e um cimento resinoso / Effect of thermocycling on the bond strength of a glass-infiltrated ceramic and a resin luting cement

O objetivo deste estudo foi avaliar o efeito da ciclagem térmica sobre a resistência de adesäo entre a superfície da cerâmica In-Ceram Alumina (VITA) e o cimento resinoso Panavia F (Kuraray). Foram confeccionados quatro blocos de cerâmica In-Ceram com dimensöes de 5x6x6mm. Uma das faces com 6x6mm de cada bloco cerâmico, após condicionamento com o sistema Cojet (ESPE-3M) (jateamento com óxido de alumínio/jateamento com óxido de sílica/ silanizaçäo) foi cimentada com Panavia F, sob peso constante de 750g, a outro bloco idêntico de resina composta Clearfil AP-X (Kuraray). Os blocos de resina foram obtidos por meio de duplicaçäo daqueles de cerâmica a partir de moldes com silicona de adiçäo Express (3M). Os quatro conjuntos formados por cerâmica, cimento e resina foram seccionados em 20 corpos-de-prova com forma de palitos, de modo que a regiäo adesiva apresentasse 1mm2 de área. Dois grupos (n=10) foram constítuidos: G1- estocagem por 7 dias em água deionizada à 36 2ºC; G2- 1500 ciclos entre 5ºC e 55ºC com intervalos de 30 segundos. A seguir, foi realizado o teste de microtraçäo em máquina de ensaio universal (EMIC) com velocidade de 0,5 mm/min. Os resultados mostraram que os valores médios de tensäo de ruptura (MPa) para o grupo G2: (22,815 5,254) näo tiveram diferenças estatisticamente significantes daqueles do grupo G1: (25,628 3,353) (t= 1,427; gl = 18; p-valor = 0,171), ao nível de significância de 5 por cento. A partir destes resultados, entendemos lícito concluir que o efeito da ciclagem térmica näo produziu alteraçöes estatisticamente significantes nos valores da resistência adesiva

Avaliaçäo clínica de restauraçöes de lesöes cervicais näo cariosas / Clinical evaluation of restorations in non-carious cervical lesions

Avaliou-se o desempenho clínico de um sistema restaurador adesivo (Excite - Tetric Ceram/ Vivadent) e do cimento de ionômero de vidro modificado por resina (Vitremer/ 3M) na restauraçäo de lesöes cervicais näo cariosas por meio do sistema de avaliaçäo do USPHS modificado. Um total de setenta restauraçöes, trinta e cinco por material, foi realizado por um único operador em trinta pacientes voluntários com idades de 23 a 68 anos. Previamente à execuçäo das restauraçöes, foi realizada uma profilaxia com pedra-pomes e água a fim de remover quaisquer resíduos. As lesöes cervicais näo foram submetidas a qualquer tipo de preparo cavitário, sendo restauradas sob isolamento absoluto e de acordo com as instruçöes do fabricante. Todas as restauraçöes foram avaliadas pelo método direto por dois examinadores nos intervalos de tempo estipulados: inicial (baseline), 6 meses, 1 ano e 2 anos usando os critérios de retençäo, integridade marginal, descoloraçäo marginal, manutençäo da forma anatômica (desgaste), cárie secundária e sensibilidade pós-operatória. Ao final de dois anos, os resultados de restauraçöes clinicamente satisfatórios (escores Alfa e Bravo) obtidos para a resina composta e cimento de ionômero de vidro modificado por resina foram respectivamente: retençäo (79 por cento, 100 por cento); integridade marginal (100 por cento, 100 por cento); descoloraçäo marginal (100 por cento, 100 por cento); desgaste (96 por cento, 100 por cento); cárie secundária (100 por cento, 100 por cento) e sensibilidade pós-operatória (100 por cento, 100 por cento). Os resultados foram submetidos à análise estatística com o teste exato de Fisher ou o teste Qui-quadrado de Pearson com nível de significância de 5 por cento (p<0,05). As comparaçöes intragrupos foram realizadas com o teste de McNemar com nível de significância de 5 por cento. Com base na análise estatística dos resultados concluiu-se que houve diferença estatisticamente significante entre os materiais no critério retençäo no período de 2 anos, sendo que nos demais critérios os dois materiais näo apresentaram diferenças estatisticamente significante

Avaliaçäo, in vitro, da açäo cariostática de materiais restauradores estéticos em esmalte bovino, sob condiçöes de sevreo desafio cariogênico / In vitro evaluation of cariostatic action of bovine aesthetic restorative materials by severe cariogenic challenge

Considerando-se que o aparecimento de lesöes de cárie ao redor de restauraçöes é um fato clinicamente relevante e que a utilizaçäo de materiais restauradores liberadores de flúor é importante para inibir o aparecimento destas lesöes, este trabalho teve por objetivo investigar, in vitro, a açäo cariostática de alguns materiais restauradores estéticos. Cavidades padronizadas foram preparadas no centro de blocos dentes bovinos hígidos ou com lesäo incipiente de cárie artificial. Os espécimes foram restaurados com: um cimento de ionômero de vidro convencional (Ketac Molar); um cimento de ionômero de vidro modificado por resina (Vitremer); uma resina composta modificada por poliácidos (Dyract AP) e uma resina convencional (Z-250). Além dos espécimes restaurados, outros quatro grupos correspondentes a controles também foram avaliados. Em seguida todos os grupos, com exceçäo de dois dos controles, foram submetidos a ciclagens de desmineralizaçäo e remineralizaçäo durante 14 dias, simulando situaçäo de severo desafio cariogênico. Após este procedimento, os blocos foram seccionados longitudinalmente através do centro das restauraçöes e a perda mineral foi avaliada por meio de testes de microdureza Knoop em secçäo longitudinal, aplicados em três diferentes distâncias das paredes cavitárias / margem da restauraçäo e em oito profundidades distintas em relaçäo à superfície externa do esmalte. A análise estatística dos resultados (p < 0,05) mostrou diferenças significantes entre os grupos, embora nenhum dos materiais estudados tenha sido capaz de impedir completamente a instalaçäo da lesäo. O material Vitremer demonstrou a melhor açäo cariostática em esmalte bovino hígido. Os materiais Ketac Molar, em esmalte hígido ou desmineralizado, assim como o Vitremer em esmalte desmineralizado, apresentaram potencial cariostástico intermediário. A resina composta Z-250 e o compômero Dyract AP näo demonstraram efeitos cariostáticos. Concluí-se portanto, que os cimentos de ionômero de vidro apresentaram açäo cariostática superior aos demais materiais estudados

Avaliaçäo em microscopias óptica e eletrônica de varredura da adaptaçäo de três cimentos endodônticos à dentina radicular submetida à açäo prévia do laser de ER: YAG, EDTA e soluçäo salina fisiológica / Optical and scanning electron microscopy evaluations of three endodontic sealers adaptation to dentin root subject to the previus action of ER: YAG laser, EDTA and saline solution

A adaptaçäo do Ketac-Endo, AH Plus e Endométhasone, à dentina radicular submetida à açäo prévia do laser de Er: YAG, EDTA a 17 por ecnto e soluçäo salina fisiológica a 0,9 por cento foi estudada pelas microscopias óptica a eletrônica de varredura. Noventa caninos humanos extraídos foram instrumentados pela técnica escalonada de memória, irrigados com hipoclorito de sódio a 1 por cento, e divididos em três grupos de 30. No grupo A, empregou-se o laser de Er:YAG intracanal, com energia real de 44mJ, 10 pps, durante dez segundos, sob refrigeraçäo a ar, com movimentos circulares no sentido apicocoronário, seguido de irrigaçäo com 20ml de soluçäo salina fisiológica a 0,9 por cento. No grupo B, empregaram-se 5ml de EDTA a 17 por cento durante cinco minutos, seguido de irrigaçäo com soluçäo salina fisiológica a 0,9 por cento. No grupo C, empregaram-se 20ml de soluçäo salina fisiológica a 0,9 por cento. Após secagem e armazenagem em soluçäo salina fisiológica a 0,9 por cento durante 48 horas, os canais foram obturados pela técnica clássica, seguida da condensaçäo lateral ativa da guta-percha e comprovaçäo radiográfica. Foram vedados com Cimpat no terço cervical e forame apical, e as raízes armazenadas em soluçäo salina fisiológica a 0,9 por cento em umidade de 100 por cento a 37ºC, durante 30 dias. Em seguida, foram seccionadas transversalmente a 5mm do ápice radicular e fixadas em discos de resina epóxica para a análise nas microscopias óptica e eletrônica de varredura. Para a análise em microscopia eletrônica de varredura, as secçöes apicais foram moldadas com Aquasil e os moldes obtidos foram metalizados. As fotos obtidas pelas microscopias foram escaneadas e transferidas para o Sigma Scan para mensuraçäo das áreas preenchidas pelos materiais obturadores e das possíveis fendas entre material obturador e parede do canal radicular. Diante dos resultados concluiu-se que: 1- O laser de Er:YAG prejudicou a adaptaçäo de todos os cimentos, o EDTA melhorou a adaptaçäo do Endométhasone e do AH Plus e a soluçäo salina fisiológica a 0,9 por cento melhorou a adaptaçäo do Ketac-Endo. 2- O Endométhasone apresentou a pior adaptaçäo. 3- A microscopia eletrônica de varredura propiciou melhor visualizaçäo das fendas

Capacidade seladora apical de cimentos endodônticos ionoméricos / Apical sealing ability of ionomeric endodontic sealers

O objetivo desse trabalho foi avaliar a capacidade seladora apical de dois cimentos endodônticos ionôméricos, Ketac Endo e Vidrion Endo, comparando-os ao Sealer 26. A metodologia utilizada foi infiltraçäo apical com o uso do corante azul de metileno a 1 por cento em obturaçöes pela técnica do cone único em raízes de dentes extraídos. Os resultados mostraram näo haver diferença estatística entre a infiltraçäo dos grupos dos cimentos ionoméricos quando comparados aos pares (Teste de Student-Newman-Keuls), porém ela ocorreu entre esses e o Sealer 26, que apresentou as menores médias de infiltraçäo (p<0,05)

Resistência ao cisalhamento de agentes cimentantes / Punch shear strength of luting cements

Estudos laboratoriais säo importantes para facilitar o entendimento do comportamento clínico dos materiais e úteis para explicar as falhas. O objetivo deste estudo foi comparar a resistência coesiva de agentes cimentantes submetidos a tensöes de cisalhamento (punch shear test). Discos medindo 1,4 cm de diâmetro por 1,5 mm de espessura foram preparados dos cimentos de ionômero de vidro Shofu (tipo I), Advance e Fuji (tipo I) e testados em máquina universal de testes nos períodos de 7 minutos, 30 minutos e 24 horas após a mistura. Todos materiais apresentaram um significante aumento de resistência entre os períodos (p<0,05). No período de 24 horas, o cimento Shofu apresentou uma resistência significantemente maior do que os cimentos Advance e Fuji. O cimento Advance näo pode ser testado no período de 7 minutos devido a sua consistência inicial näo permitir o teste